CN106830812A - A kind of lightweight heat-proof artificial board - Google Patents
A kind of lightweight heat-proof artificial board Download PDFInfo
- Publication number
- CN106830812A CN106830812A CN201710162634.0A CN201710162634A CN106830812A CN 106830812 A CN106830812 A CN 106830812A CN 201710162634 A CN201710162634 A CN 201710162634A CN 106830812 A CN106830812 A CN 106830812A
- Authority
- CN
- China
- Prior art keywords
- parts
- artificial board
- lightweight heat
- proof artificial
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of lightweight heat-proof artificial board, the invention is the flyash by cement, glass microballoon, latex powder, cellulose ether, and biomass composite etc. is mixed with and forms.Lightweight heat-proof artificial board of the invention, mainly with cement, the main Binder Materials of flyash, and latex powder is added as supplementary cementitious material, effectively with reference to the characteristics of organic and inorganic coagulation material, enhance timber intensity.Glass microballoon and biomass composite are with the addition of in addition, it is effectively utilized agricultural wastes, greatly reduce the weight of sheet material, and possess preferable heat-insulated, soundproof effect, can be widely used in roofing board, partition plate, floor, exterior wall cover plate, movable dwellings, house sound panel, highway sound panel, building wall block, building template and interior decoration.
Description
Technical field
The present invention relates to chemical field, and in particular to a kind of lightweight heat-proof artificial board.
Background technology
Wood-based plate is a kind of with portland cement as cementing material, with wood particle（Or cotton stalk, waste of flax, beans bar, straw etc.
String）Be reinforcement material, add water and chemical assistant, blended stirring, airflow pavement, laminate shaping, steam test maintenance and
The operations such as artificial drying and the artificial board that is made.Wood-based plate has good physical and mechanical property, waterproof fireproofing performance and adds
Work performance, is the novel wall material and decorating and renovating material of a kind of high comprehensive performance, is widely used as various buildings
Ceiling suspended ceiling plate, non-load bearing inner partition wall plate, floor plate, roof boarding, Side fascia and sentry box, retail kiosk, prefabricated house etc. set temporarily
The cladding applied, or manufacture the optimal base material of senior antistatic floor.
The content of the invention
Present invention aim at, there is provided a kind of lightweight heat-proof artificial board, the technical solution adopted by the present invention is as follows：
A kind of lightweight heat-proof artificial board, it is characterised in that be mixed with by weight percentage by following components and formed：
Cement 15-35 parts
Flyash 5-20 parts
Glass microballoon 10-20 parts
Latex powder 1-5 parts
Cellulose ether 1-3 parts
Biomass composite 25-50 parts.
One of preferably, described cement is Portland cement.
One of preferably, 100-180 microns of described particle size of glass microspheres scope, bulk density is in 0.1-0.2
Gram/cc.
One of preferably, described cellulose ether is the mpa.s of viscosity 18-20 ten thousand.
One of preferably, described biomass composite includes discarded bamboo powder, peanut shell, straw.
The present invention is relative to the beneficial effect of prior art：Lightweight heat-proof artificial board of the invention, mainly with cement,
The main Binder Materials of flyash, and latex powder is added as supplementary cementitious material, effectively with reference to organic and inorganic coagulation material
The characteristics of, enhance timber intensity.Glass microballoon and biomass composite are with the addition of in addition, are effectively utilized agriculture waste
Thing, greatly reduces the weight of sheet material, and possesses preferable heat-insulated, and soundproof effect can be widely used in roofing board, partition wall
Plate, floor, exterior wall cover plate, movable dwellings, house sound panel, highway sound panel, building wall block, building template and room
In interior trim.
Specific embodiment
Design of the invention and the technique effect for producing are clearly and completely described below with reference to embodiment, with
It is completely understood by the purpose of the present invention, feature and effect.Obviously, described embodiment is that a part of the invention is implemented
Example, rather than whole embodiments, based on embodiments of the invention, those skilled in the art is not before creative work is paid
Obtained other embodiment is put, the scope of protection of the invention is belonged to.
Embodiment 1：A kind of lightweight heat-proof artificial board, is mixed with and formed by weight percentage by following components：
22 parts of cement
14 parts of flyash
12 parts of glass microballoon
3 parts of latex powder
2 parts of cellulose ether
27 parts of biomass composite.
Embodiment 2：A kind of lightweight heat-proof artificial board, is mixed with and formed by weight percentage by following components：
18 parts of Portland cement
15 parts of flyash
17 parts of glass microballoon
3 parts of latex powder
2 parts of cellulose ether
45 parts of biomass composite.
Wherein, 100-180 microns of above-mentioned particle size of glass microspheres scope, bulk density is at 0.1-0.2 grams/cc.
Wherein, above-mentioned cellulose ether is the mpa.s of viscosity 18-20 ten thousand.
Wherein, above-mentioned biomass composite includes 25 parts of discarded bamboo powders, 10 parts of peanut shells, 10 parts of straws.
Better embodiment of the invention is illustrated above, but the invention is not limited to the implementation
Example, those of ordinary skill in the art can also make a variety of equivalent modifications or replace on the premise of without prejudice to spirit of the invention
Change, these equivalent modifications or replacement are all contained in the application claim limited range.
Claims (5)
1. a kind of lightweight heat-proof artificial board, it is characterised in that be mixed with by weight percentage by following components and formed：
Cement 15-35 parts
Flyash 5-20 parts
Glass microballoon 10-20 parts
Latex powder 1-5 parts
Cellulose ether 1-3 parts
Biomass composite 25-50 parts.
2. lightweight heat-proof artificial board according to claim 1, it is characterised in that described cement is normal silicate water
Mud.
3. lightweight heat-proof artificial board according to claim 1, it is characterised in that described particle size of glass microspheres scope
100-180 microns, bulk density is at 0.1-0.2 grams/cc.
4. lightweight heat-proof artificial board according to claim 1, it is characterised in that described viscosity of cellulose ether is in 18-
200000 mpa.s.
5. lightweight heat-proof artificial board according to claim 1, it is characterised in that described biomass composite is included
Discarded bamboo powder, peanut shell, straw.