CN101851079B - 一种复合材料及其制作方法 - Google Patents
一种复合材料及其制作方法 Download PDFInfo
- Publication number
- CN101851079B CN101851079B CN2010101472567A CN201010147256A CN101851079B CN 101851079 B CN101851079 B CN 101851079B CN 2010101472567 A CN2010101472567 A CN 2010101472567A CN 201010147256 A CN201010147256 A CN 201010147256A CN 101851079 B CN101851079 B CN 101851079B
- Authority
- CN
- China
- Prior art keywords
- parts
- composite material
- cement
- water
- acrylic emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供了一种新型复合材料及其制作方法，该建筑材料解决了普通石膏装饰材料存在的不防水、易损坏、难上色，以及水泥制品存在的体重、成本高、产品粗糙等缺陷，本发明通过以下技术手段来实现：丙烯酸乳液8-12份、水泥35-45份、沙20-30份、水15-20份；优选的是按照下述重量份数配比：丙烯酸乳液9-11份、水泥38-42份、沙18-22份、水15-20份，将这些原料混合搅拌均匀，通过模具制得不同的建筑装饰产品，得到的装饰品不仅具有仿木、仿石色泽，而且具有防水、防火、高强度、低成本、表面细密、光滑、光亮等优良性能。
Description
技术领域
本发明涉及一种建筑材料。
背景技术
随着人们生活水平的提高，各种各样的建筑装饰品进入千家万户，越来越受到消费者的欢迎。普通石膏生产的装饰材料存在不防水、易损坏、难上色等缺陷，而水泥浇筑的装饰材料又存在质量重、成本高、成模得到的产品不光滑等缺陷。随着人们生活水平的提高，人们对建筑装饰产品的需求量越来越高，对质感要求也越来越高。
发明内容
本发明旨在提供一种新型复合材料及其制作方法，采用该复合材料生产得到的装饰品不仅具有仿木、仿石色泽，而且具有防水、防火、高强度、低成本、表面细密、光滑、光亮等优良性能。
为实现以上目的，本发明通过以下技术手段实施：
一种新型复合材料，它是由下述重量份数配比的原料制成的复合材料：丙烯酸乳液8-12份、水泥35-45份、沙20-30份、水15-20份。优选各原料的重量份数配比为：丙烯酸乳液9-11份、水泥38-42份、沙18-22份、水15-20份。
为了使制造出来的装饰材料具有很好的光亮度，可以加入8-15份的石英砂。
为了减轻复合材料的重量，可以加入33-38份的轻质材料，轻质材料可以是木屑、锯末、珍珠岩、桔杆中的一种或两种以上的混合物。
该新型复合材料可以按照以下方法进行生产：将各组分按照配比称重配好，充分搅拌均匀制得新型复合材料，根据具体用途，采用不同形状和结构的模具进行浇注成型晾干即可生产得到各种家居装饰品、建筑装饰材料等。
有益效果
①本发明新型复合材料生产工艺简单，成本低，得到的装饰品及建筑装饰材料具有仿木、仿石色泽，且呈现出美观细腻的纹理、富有弹性、色彩自然、给人以典雅、亲切、柔和之感。
②本发明新型复合材料中含有的石英砂具有较高的稳定性、较强的抗酸性、耐腐蚀性以及较好的耐火性，提高了该复合材料的实用价值，延长了使用寿命，最主要的是石英晶体具有优良的光学性能，可使生产出来的产品具有很好的光亮度，提升了产品的美观度。
③本发明新型复合材料用于生产建筑装制品，所得的建筑装饰品不需经过高温烧结，只要在常温下自然风干即可，节约了能源。
④本发明的新型复合材料中添加了丙烯酸乳液和水泥，二者硬化后相互贯穿，形成的聚合物网络阻止了混合物中微裂缝的生长，使制得的建筑装饰品具有很高的强度，满足建筑行业的使用要求。
⑤本发明的新型复合材料所制得的建筑装饰品具有很好的防水性，其中的丙烯酸乳液使水泥和骨料形成强有力的粘结性，并产生较强的结晶网，从而防水性能得到明显改善，具有很好的防水效果。
⑥本发明的新型复合材料所制得的建筑装饰品具有很好的防火性和阻燃作用。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
实施例1
按下述配比称取原料：丙烯酸乳液8kg、水泥35kg、沙20kg、水15kg。
按照以上配比充分混合均匀制得新型复合材料，通过将制得的新型复合材料倒入模具中加压成型，晾干后脱去模具制得家居装饰品，其外观细腻，防水性好，强度高，并且经济环保。采用以下方法进行测试：
①将得到的装饰品置于明火环境下4分钟，该装饰品表面无裂痕，只有轻微灼烧痕迹。
②将得到的装饰品称重后放入水中浸泡14小时，取出后再称重，其质量没有增加，该装饰品表面依然保持平整光滑、无裂痕。
③自由落体实验：把重量相同的砖块、普通聚合水泥和本产品在4米高的地方同时做自由落体运动，结果是普通聚合水泥出现断裂，砖块有碎块脱落，新型复合材料所制成的建筑装饰品没有出现裂痕和断裂，并且基本保持原形状。由上述实验得：新型复合材料所制成的建筑装饰品的强度大于砖块、普通聚合水泥。
实施例2
按下述配比称取原料：丙烯酸乳液10kg、水泥40kg、沙25kg、水20kg。
按照以上配比充分混合均匀制得新型复合材料，通过将制得的新型复合材料倒入模具中加压成型，晾干后脱去模具制得护栏装饰柱，其外观细腻，防水性好，强度高，并且经济环保。采用以下方法进行测试：
①将得到的装饰品置于明火环境下5分钟，该装饰品表面无裂痕，只有轻微灼烧痕迹。
②将得到的装饰品称重后放入水中浸泡16小时，取出后再称重，其质量没有增加，该装饰品表面依然保持平整光滑、无裂痕。
③自由落体实验：把重量相同的砖块、普通聚合水泥和本产品在5米高的地方同时做自由落体运动，结果是普通聚合水泥出现断裂，砖块有碎块脱落，新型复合材料所制成的建筑装饰品没有出现裂痕和断裂，并且基本保持原形状。由上述实验得：新型复合材料所制成的建筑装饰品的强度大于砖块、普通聚合水泥。
实施例3
按下述配比称取原料：丙烯酸乳液10kg、水泥40kg、沙25kg、水20kg、石英砂10kg。
按照以上配比充分混合均匀制得新型复合材料，通过将制得的新型复合材料倒入模具中加压成型，晾干后脱去模具制得观赏性仿石雕，其外观光亮细腻，防水性好，强度高，并且经济环保。采用以下方法进行测试：
①将得到的装饰品置于明火环境下5分钟，该装饰品表面无裂痕，只有轻微灼烧痕迹。
②将得到的装饰品称重后放入水中浸泡16小时，取出后再称重，其质量没有增加，该装饰品表面依然保持平整光滑、无裂痕。
③自由落体实验：把重量相同的砖块、普通聚合水泥和本产品在5米高的地方同时做自由落体运动，结果是普通聚合水泥出现断裂，砖块有碎块脱落，新型复合材料所制成的建筑装饰品没有出现裂痕和断裂，并且基本保持原形状。由上述实验得：新型复合材料所制成的建筑装饰品的强度大于砖块、普通聚合水泥。
实施例4
按下述配比称取原料：丙烯酸乳液10kg、水泥40kg、沙25kg、水20kg、石英砂10kg、由木屑10kg、锯末5kg、珍珠岩12kg、桔杆8kg组成的轻质材料。
按照以上配比充分混合均匀制得新型复合材料，通过将制得的新型复合材料倒入模具中加压成型，晾干后脱去模具制得观赏性仿木雕，其外观光亮细腻，防水性好，强度高，并且经济环保。采用以下方法进行测试：
①将得到的装饰品置于明火环境下5分钟，该装饰品表面无裂痕，只有轻微灼烧痕迹。
②将得到的装饰品称重后放入水中浸泡16小时，取出后再称重，其质量没有增加，该装饰品表面依然保持平整光滑、无裂痕。
③自由落体实验：把重量相同的砖块、普通聚合水泥和本产品在5米高的地方同时做自由落体运动，结果是普通聚合水泥出现断裂，砖块有碎块脱落，新型复合材料所制成的建筑装饰品没有出现裂痕和断裂，并且基本保持原形状。由上述实验得：新型复合材料所制成的建筑装饰品的强度大于砖块、普通聚合水泥。
Claims (3)
1.一种复合材料，其特征在于，它是由下述重量份数配比的原料制成的复合材料：丙烯酸乳液8-12份、水泥35-45份、沙20-30份、水15-20份、木屑、锯末、珍珠岩、秸杆中的一种或两种以上组合的轻质材料33-38份。
2.一种复合材料，其特征在于，按重量份数计算，由下述原料制成：丙烯酸乳液8-12份、水泥35-45份、沙20-30份、水15-20份、木屑、锯末、珍珠岩、秸杆中的一种或两种以上组合的轻质材料33-38份，石英砂8-15份。
3.一种权利要求1或2所述的复合材料的制造方法，其特征在于，将各组分按照计量标准称重配好，充分混合均匀制得复合材料。